DuPont Elvaloy® 3717 AC Ethylene and 17% Butyl Acrylate Copolymer
| Category | Polymer , Film , Thermoplastic , Ethylene Butyl Acrylate |
| Manufacturer | DuPont Packaging and Industrial Polymers |
| Trade Name | Elvaloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Elvaloy® 3717 AC Ethylene and 17% Butyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Elvaloy® 3717 AC can be used for coextrusion, compounding and injection molding. In coextrusion, it can be used to improve sealing; in compounding, to improve low temperature and impact properties. Elvaloy® 3717 AC also is very suitable as a carrier polymer in masterbatches.Elvaloy® 3717 AC is easily processed on standard equipment used for low density polyethylene.Information provided by DuPont.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 - ISO 1183 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 - ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | ASTM D2240 - ISO 868 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 - ISO 868 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | 500 mm/min; ASTM D638 - ISO 527-2 |
| Elongation at Break | 850 % | 850 % | 500 mm/min; ASTM D638 - ISO 527-2 |
| Tensile Modulus | 0.0400 GPa | 5.80 ksi | 1 mm/min; ASTM D638 - ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 96.0 °C | 205 °F | By DSC; ASTM D3418 - ISO 3146 |
| Vicat Softening Point | 55.0 °C | 131 °F | A<sub>50</sub> (10N); ASTM D1525 - ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 °C | 302 °F | Extrusion lamination and extrusion coating |
| 150 °C | 302 °F | Cast film | |
| 150 °C | 302 °F | Blown film | |
| Middle Barrel Temperature | 160 °C | 320 °F | Blown film |
| 210 °C | 410 °F | Cast film | |
| 220 °C | 428 °F | Extrusion lamination | |
| Front Barrel Temperature | 170 °C | 338 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Adapter Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast Film | |
| 290 °C | 554 °F | Extrusion lamination | |
| Die Temperature | 180 °C | 356 °F | Blown film |
| 250 °C | 482 °F | Cast film | |
| 290 °C | 554 °F | Extrusion lamination |
| Descriptive Properties | Value | Comments |
|---|---|---|
| BA-Content | 17 wt.% | DuPont Method |
Users viewing this material also viewed the following:
- Northstar Polymers MPN-055 Polyether Prepolymer
- Kuraray HYBRAR® PP2 Thermoplastic Rubber-Polypropylene Blend
- Multibase Multi-Flex® G 7680 TPE Styrene Ethylene Butylene Styrene Block Copolymer
- Teknor Apex APEX® 2560-H Polyvinyl Chloride, Flexible
- Zotefoams Plastazote® LD33LC Low Density Polyethylene Foam, Large Cell
- Dow Corning SYL-OFF® PMCPSL 11 Crosslinker
- Dow AFFINITY™ PL 1845 Polyolefin Plastomer
- Haynes 242® alloy, hot rolled plate, annealed and aged
Copyright © lookpolymers.com All Rights Reserved