ExxonMobil LLDPE LL 8450.31 Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Exxon Chemical
Trade Name LLDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LLDPE LL 8450.31 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 8450 is a linear low density hexene copolymer designed to offer excellent stiffness, processability, whiteness and ESCR. They are ideally suited for applications that require the optimum balance of stiffness and processability. Availability: Latin America, North America and South America Additive: Stabilizer: YesLong Term UV-8 Applications: Consumer ArticlesJunction BoxesPlayground EquipmentPotable Water TanksSmall Storage BoxesInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.937 g/cc
0.0339 lb/in³
ExxonMobil method
ESCR 100% Igepal® >= 1000 hour
>= 1000 hour
F50; ASTM D1693B
ESCR 10% Igepal® 190 hour
190 hour
F50; ASTM D1693B
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.9 MPa
2600 psi
2.0 in/min; ASTM D638
Elongation at Yield 20 %
20 %
2.0 in/min; ASTM D638
Flexural Modulus, 1% Secant 758 MPa
110000 psi
ASTM D638
Impact Test 77.3 J

@Thickness 3.17 mm,
Temperature -40.0 °C
57.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM
183 J

@Thickness 6.35 mm,
Temperature -40.0 °C
135 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM
Thermal Properties Metric English Comments
Melting Point <= 261 °C
<= 502 °F
Peak Melting Point; ExxonMobil method
Deflection Temperature at 0.46 MPa (66 psi) 61.1 °C
142 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 37.8 °C
100 °F
ASTM D648