SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
| 64.0 MPa | 9280 psi | ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Tensile Modulus | 3.45 GPa | 500 ksi | 50 mm/min; ASTM D638 |
| 3.75 GPa | 544 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| 116 MPa | 16800 psi | ASTM D790 | |
| Flexural Modulus | 3.51 GPa | 509 ksi | ASTM D790 |
| 3.52 GPa | 511 ksi | ISO 178 | |
| Izod Impact, Notched | 0.230 J/cm | 0.431 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 1.00 J | 0.738 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 52.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 52.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.70 mm |
V-0 @Thickness 0.0669 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymer Industries Densetec HMW Sheet
- Kazanorgsintez 102-23 Composition of Low Density Polyethylene, Crack-Proof
- Solvay AMPHIONIC® XL Surfactant
- A. Schulman SCHULADUR® A GF10 10% Glass Fiber Reinforced PBT
- Hexcel® HexWeb® HRP/F50 - 4.5 Nonmetallic Flex-Core Honeycomb
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N774 Filler
- Asia International Enterprise (Hong Kong) 30G6 Polybutylene terephthalate, 30% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved