NOVA Chemicals Sclair® 11L2B Octene LLDPE Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® 11L2B Octene LLDPE Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Properties. Features: Low gel, excellent seal characteristics, easy processability.Applications: Specialty lamination, co-extrusion of food and liquid packaging.Data provided by the manufacturer.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D792
Melt Flow 0.72 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.72 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.00 MPa
1310 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 624 %
624 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Secant Modulus, MD 0.203 GPa
29.4 ksi
ASTM D882
Secant Modulus, TD 0.210 GPa
30.5 ksi
ASTM D882
Coefficient of Friction >= 0.40
>= 0.40
ASTM D1894
Elmendorf Tear Strength, MD 18.0 g/micron
457 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 23.0 g/micron
584 g/mil
ASTM D1922
Dart Drop 8.00 g/micron
203 g/mil
F 50; ASTM D1709/A
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD 21.0 MPa
3050 psi
ASTM D882
Optical Properties Metric English Comments
Haze 11 %

@Thickness 0.0250 mm
11 %

@Thickness 0.000984 in
ASTM D1003
Gloss 51 %
51 %
45°; 1 mil; ASTM D1894
Processing Properties Metric English Comments
Melt Temperature 210 - 220 °C
410 - 428 °F