Braskem LL5801N LLDPE Blown Film Extrusion Polyethylene Copolymer
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LL5801N LLDPE Blown Film Extrusion Polyethylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The LL5801N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid, antioxidant, slip, and antiblocking additives. Its applications include: stretch film; and laminating and specialties made of high strength films. The LL5801N resin should be processed on specific extruders for LLDPE. The best results are obtained at a melt temperature within the range of 200 to 220ºC and blends with maximum ratio of 30% LLDPE. Recommended blow up ratio: 1.8 to 3.0:1.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 920 % | 920 % | ASTM-D882 |
| Film Elongation at Break, TD | 1240 % | 1240 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 330 g | 330 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 770 g | 770 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 13.2 g/micron | 335 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 30.8 g/micron | 782 g/mil | ASTM-D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | ASTM-D1709 |
| Dart Drop Test | 200 g | 0.441 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 150 MPa | 21800 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % | 8.0 % | ASTM-D1003 |
| Gloss | 114 % | 114 % | Angle 60°; ASTM-D2457 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 N PP, basic type
- Pacific Sintered Materials SS-316-RD 316L Stainless Steel Powdered Metal
- BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry) (discontinued **)
- LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose
- Teknor Apex Telcar® TL EF-6162 Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- Fainplast Compounds KL 101 Flexible PVC, Insulation for High Temperatures Lead Free
- Fainplast Compounds KL 77 Flexible PVC, Insulation for High Temperatures Lead Free
- Braskem LQ 0518/30 LLDPE Blown Film Extrusion Polyethylene
- Bostik 6327 Color Blending, Low Viscosity, Flexible EVA Glue Stick
Copyright © lookpolymers.com All Rights Reserved