Dow DOWLEX™ 2071D Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2071D Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good processability at narrow die gaps Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Slip Level | 850 ppm | 850 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 13.15 MPa | 1907 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 15.73 MPa | 2281 psi | ASTM D882 |
| Film Elongation at Break, MD | 624 % | 624 % | ASTM D882 |
| Film Elongation at Break, TD | 696 % | 696 % | ASTM D882 |
| Secant Modulus, MD | 0.2682 GPa | 38.90 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.34129 GPa | 49.501 ksi | 2% Secant; ASTM D882 |
| Impact | 48 | 48 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method |
| 1290 | 1290 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 | |
| 1410 | 1410 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 405 g | 405 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1141 g | 1141 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 7.972 g/micron | 202.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.46 g/micron | 570.5 g/mil | ASTM D1922 |
| Dart Drop Test | 281 g | 0.620 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.21 MPa | 5252 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.12 MPa | 4804 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 15.1 % | 15.1 % | ASTM D1003 |
| Gloss | 49.6 % | 49.6 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Nylene® Norpex® AX20MR , 20% Mineral Reinforced Polyphenylene Ether
- SABIC Innovative Plastics Lexan® OQ2220 PC
- PolyOne Geon™ Vinyl Flexible WR3090S Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kolon KOPA® KN173HI3R High Impact Nylon 6
- Lucas-Milhaupt Silvaloy® 5 Brazing Alloy
- DuPont Elvanol® 50-14 Polyvinyl Alcohol Partially Hydrolyzed General Purpose Grade
- Covestro Bayflex® XGT-140 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- China Tungsten NT2 Titanium Carbide and Nitride Based Carbides
- Polykemi AB POLYelast TPE Z557 Thermoplastic Elastomer, SEBS-based
- Overview of materials for Polypropylene Glass Bead Filled
Copyright © lookpolymers.com All Rights Reserved