Dow DNDA-8350 NT 7 Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DNDA-8350 NT 7 Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DOW DNDA-8350 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 5.0 hour @Temperature 50.0 °C |
5.0 hour @Temperature 122 °F |
F<sub>50</sub>; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| Melt Index of Compound | 55 g/10 min @Load 2.16 kg, Temperature 190 °C |
55 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 52 | 52 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 9.65 MPa | 1400 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.421 GPa | 61.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 189 kJ/m² | 90.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Crystallization Temperature | 109 °C | 228 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ3420 PC
- BASF Capron® B135ZP Nylon 6 (DAM) (discontinued **)
- Iran Petrochemical (PCC) EP2C 37 F Polypropylene
- Solvay Specialty Polymers Hyflon® AD 60 Perfluoropolymer
- SPS Guang Zhou FILLMAâ„¢ 5002F30B Mineral Filled Polypropylene
- Westlake Hifor LT74147 Linear Low Density Polyethylene
- Ashley Polymers Ashlene® 981S Nylon 612
- 3M 9085 Ultra High Temperature 100 HT Adhesive Transfer Tape
- AK Steel TRAN-COR® H-0 CARLITE® DR® Grain Oriented Electrical Steel
- LATI Latilub 67-10STE21 G/20 PA66, 20% Glass Fiber Reinforced, Silicone/PTFE Filled
Copyright © lookpolymers.com All Rights Reserved