Diamond Polymers Softflex® 1302 Thermoplastic Elastomer Alloy
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | Softflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers Softflex® 1302 Thermoplastic Elastomer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.904 g/cc | 0.904 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.038 cm/cm @Thickness 3.17 mm |
0.038 in/in @Thickness 0.125 in |
Transverse to Flow; ASTM D955 |
| 0.0413 cm/cm @Thickness 3.17 mm |
0.0413 in/in @Thickness 0.125 in |
Direction of Flow; ASTM D955 | |
| Melt Flow | 0.50 g/10 min @Load 1.00 kg, Temperature 235 °C |
0.50 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 68 - 78 | 68 - 78 | ASTM D2240 |
| Tensile Strength, Yield | 3.50 MPa | 508 psi | chs 20 in/min; 100% elongation; ASTM D412 |
| 4.04 MPa | 586 psi | chs 20 in/min; 300% elongation; ASTM D412 | |
| 37.1 MPa | 5380 psi | chs 20 in/min; 50% elongation; ASTM D412 | |
| 37.11 MPa | 5382 psi | chs 20 in/min; ASTM D412 | |
| Elongation at Break | 295 % | 295 % | ASTM D412 |
| Flexural Modulus | 0.04064 GPa | 5.894 ksi | ASTM D790 |
| Gardner Impact | >= 36.2 J @Temperature -30.0 °C |
>= 26.7 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
| Taber Abrasion, mg/1000 Cycles | 0.2625 @Load 1.00 kg |
0.2625 @Load 2.20 lb |
H22 Wheel; ASTM D3389 |
| Compression Set | 15.5 % @Temperature 22.8 °C, Time 79200 sec |
15.5 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D395 |
| 21.3 % @Temperature 70.0 °C, Time 79200 sec |
21.3 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
Users viewing this material also viewed the following:
- Nyco NYGLOS® STPO Wollastonite
- I. Stern HIPS 8 High Impact Polystyrene Injection Grade
- Gouda Vuurvast CURON 145 CC Dense Refractory Castable
- Styron EMERGEâ„¢ 4202-8 MFR Polycarbonate
- Solvay TECHNYL® A 208F PA66, DRY
- SABIC Innovative Plastics Valox® SHF4930 PBT
- Covestro Bayflex® XGT-16 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System
- Abatron L060421-1 Heat-Resistant (-75~400°F) Non-Flammable Silicone Rubber
- Bedford Plastics Glass Reinforced FR Polyester Structural Fiberglass Profiles
- Axiall Suprel® SVA 9301 Rigid PVC, Molding
Copyright © lookpolymers.com All Rights Reserved