- Diamond Polymers NPP30-0800 GF40 40% Glass Filled Homopolymer Polypropylene
Diamond Polymers NPP30-0800 GF40 40% Glass Filled Homopolymer Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Diamond Polymers NPP30-0800 GF40 40% Glass Filled Homopolymer Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm <br>@Thickness 1.59 mm |
0.0020 in/in <br>@Thickness 0.0625 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
8.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 81.0 MPa | 11700 psi | chs 0.2 in/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | chs 0.2 in/min; ASTM D638 |
| Flexural Strength | 102.7 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 6.752 GPa | 979.3 ksi | tangent; ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm <br>@Thickness 3.17 mm |
1.60 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Gardner Impact | 0.500 J <br>@Temperature 23.0 °C |
0.369 ft-lb <br>@Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | 0.125";; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Content (%) | 40 | ASTM D2584 |
Users viewing this material also viewed the following:
- Permabond HM161 Anaerobic Retaining Compound
- Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes
- SABIC Innovative Plastics LNP THERMOCOMP MF003SU PP (Europe-Africa-Middle East)
- Daikin NEOFLON NF-1000 FEP Film
- Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Conditioned (2.5% Moisture)
- 3M Dyneon™ TFM™ 2001Z PTFE
- Axiall 8906 Moldings & Extrusions Flexible PVC
- 3M Scotch-Weld™ 6111 Tan Bulk only Adhesive
- SABIC Innovative Plastics Lexan® EXL9414T PC Copolymer (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved