BCC Products Kwik Kast BC 8001 Urethane Casting
| Category | Polymer , Thermoset , Polyurethane, TS |
| Manufacturer | BCC Products |
| Trade Name | Kwik Kast |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BCC Products Kwik Kast BC 8001 Urethane Casting.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BC8001 is an advanced fast cast polyurethane tooling system. It features low viscosity, low exotherm and minimal shrinkage. It cures hard, yet more durable resulting in less brittle parts. Designed for constructing patterns, prototypes, duplications, negatives, low temperature vacuum form tools, tracing models, etc.Information provided by BCC Products, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.80 - 1.90 g/cc | 1.80 - 1.90 g/cc | |
| Brookfield Viscosity | 2200 cP @Temperature 23.9 °C |
2200 cP @Temperature 75.0 °F |
1 minute, #3 spindle @ 20 rpm |
| Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 - 87 @Temperature 23.9 °C |
83 - 87 @Temperature 75.0 °F |
|
| Tensile Strength, Ultimate | 39.3 MPa | 5700 psi | |
| Flexural Strength | 56.5 MPa | 8200 psi | |
| Compressive Strength | 91.0 MPa | 13200 psi |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 - 120 min @Temperature 24.0 °C |
1.00 - 2.00 hour @Temperature 75.2 °F |
demold time |
| Pot Life | 5.0 min @Temperature 24.0 °C |
5.0 min @Temperature 75.2 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 1:1 by weight or volume |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced
- Kazanorgsintez 107-278 Low Density Polyethylene Composition with Improved Processibility
- Lucobit Lucofin® 1413-t3 Polyolefin TPO Granules, Dark Grey
- Heatbath/Park #900 High Speed Hardening Salt
- Saint-Gobain Vitreosil® Clear Fused Quartz Tubing
- Polyplastics TOPAS® 6017 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- Toyobo E3090A Thermoplastic Polyurethane Elastomer, Extrusion Grade
- Asahi Glass Fluon® G340 PTFE Granular Powder
- Momentive Performance Materials HV 3/606 Heat Cured Rubber - High Temperature
Copyright © lookpolymers.com All Rights Reserved