Diamond Polymers DIAMALOY PC 1812 Impact Modified Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Diamond Polymers DIAMALOY PC 1812 Impact Modified Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Melt Flow 18 g/10 min
<br>@Load 3.80 kg,<br> Temperature 300 °C
 18 g/10 min
<br>@Load 8.38 lb,<br> Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 58.0 MPa
8410 psi
chs 50 mm/min; ASTM D638
Elongation at Break 110 %
110 %
chs 50 mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
chs 2 mm/min; ASTM D790
Flexural Modulus 2.27 GPa
329 ksi
chs 2 mm/min; ASTM D790
Izod Impact, Notched 3.74 J/cm
<br>@Thickness 3.17 mm,<br> Temperature -30.0 °C
 7.01 ft-lb/in
<br>@Thickness 0.125 in,<br> Temperature -22.0 °F
 ASTM D256
6.41 J/cm
<br>@Thickness 3.17 mm,<br> Temperature 23.0 °C
 12.0 ft-lb/in
<br>@Thickness 0.125 in,<br> Temperature 73.4 °F
 ASTM D256
Dart Drop, Total Energy 51.0 J
37.6 ft-lb
Peak Energy; ASTM D3763
Thermal Properties Metric English Comments
Vicat Softening Point 146 °C
<br>@Load 5.00 kg,<br> Thickness 3.17 mm
 295 °F
<br>@Load 11.0 lb,<br> Thickness 0.125 in
 ASTM D1525
Flammability, UL94 HB
<br>@Thickness 1.59 mm
 HB
<br>@Thickness 0.0625 in
HB
<br>@Thickness 3.17 mm
 HB
<br>@Thickness 0.125 in