Diamond Polymers DIAMALOY PC 1113 Impact Modified Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers DIAMALOY PC 1113 Impact Modified Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 3.80 kg,
Temperature 300 °C
 11 g/10 min

@Load 8.38 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 56.0 MPa
8120 psi
chs 50 mm/min; ASTM D638
Elongation at Break 130 %
130 %
chs 50 mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
chs 2 mm/min; ASTM D790
Flexural Modulus 2.27 GPa
329 ksi
chs 2 mm/min; ASTM D790
Izod Impact, Notched 5.34 J/cm

@Thickness 3.17 mm,
Temperature -30.0 °C
 10.0 ft-lb/in

@Thickness 0.125 in,
Temperature -22.0 °F
 ASTM D256
6.94 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 13.0 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 ASTM D256
Dart Drop, Total Energy 57.0 J
42.0 ft-lb
Peak Energy; ASTM D3763
Thermal Properties Metric English Comments
Vicat Softening Point 146 °C

@Load 5.00 kg,
Thickness 3.17 mm
 295 °F

@Load 11.0 lb,
Thickness 0.125 in
 ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
 HB

@Thickness 0.0625 in
HB

@Thickness 3.17 mm
 HB

@Thickness 0.125 in