- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Diamond Polymers ASA TWP 155
Diamond Polymers ASA TWP 155
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ASA TWP 155.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Transparent Weatherable PolymerInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 14 g/10 min @Load 3.80 kg, Temperature 230 °C |
14 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 58.29 MPa | 8454 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 339 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.6 % @Thickness 3.00 mm |
7.6 % @Thickness 0.118 in |
ASTM D1003 |
| Transmission, Visible | 85.5 % @Thickness 3.00 mm |
85.5 % @Thickness 0.118 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- Murtfeldt Original Material ”S”® Green Polyethylene
- ND Industries 360 Surface Insensitive Instant Superglue
- Plastcom SLOVAMID 6 HI/1 TLS PA6, improved strength
- Ineos Nova S-6600 High Impact Compact Polystyrene (discontinued **)
- Covestro Makrolon® CD 2005 Polycarbonate, Optical/Compact Disc Grade (discontinued **)
- Flint Hills P4G4K-205 Homopolymer Polypropylene
- Vyncolit G885 Novolac Phenolic
- Zeon Chemicals Nipol® 1072x28 Carboxylated Nitrile Elastomer
- EMS-Grivory Grivory® GVL-6H black 9915 PA*-GF60
Copyright © lookpolymers.com All Rights Reserved