PolyOne Edgetek® PE-30GF/000 WHITE High Density Polyethylene (HDPE), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PE-30GF/000 WHITE High Density Polyethylene (HDPE), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedWhitePolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.14 GPa | 600 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.50 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | Annealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 221 °C | 380 - 430 °F | Molding |
| Mold Temperature | 26.7 - 54.4 °C | 80.0 - 130 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1-0866 Polyamide 66, with aramid reinforcement, heat stabilized
- Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched
- Techmer ES Plastiblend® ABS 8005
- Total PPH 3371 Polypropylene, Oriented Film Extrusion Grade
- Formosa Plastics Formolene® 6535N Impact Copolymer Polypropylene
- A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy
- Eurotec® Tecomid® NA40 NL IL PA 6.6 impact modified
- Amco PRIMATOP HDPE 003955P Phillips Process Hexene Copolymer
Copyright © lookpolymers.com All Rights Reserved