DSM Arnite® T06 204 XL PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnite® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnite® T06 204 XL PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low Viscosity, Injection Molding, Low outgassing
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.45 % | 0.45 % | Sim. To ISO 62 |
| Moisture Absorption | 0.180 % | 0.180 % | Sim. To ISO 62 |
| Viscosity | 8000 cP @Shear Rate 100000 1/s, Temperature 270 °C |
8000 cP @Shear Rate 100000 1/s, Temperature 518 °F |
|
| 8500 cP @Shear Rate 100000 1/s, Temperature 250 °C |
8500 cP @Shear Rate 100000 1/s, Temperature 482 °F |
||
| 9000 cP @Shear Rate 100000 1/s, Temperature 230 °C |
9000 cP @Shear Rate 100000 1/s, Temperature 446 °F |
||
| 100000 cP @Shear Rate 1.00 1/s, Temperature 270 °C |
100000 cP @Shear Rate 1.00 1/s, Temperature 518 °F |
||
| 175000 cP @Shear Rate 1.00 1/s, Temperature 250 °C |
175000 cP @Shear Rate 1.00 1/s, Temperature 482 °F |
||
| 300000 cP @Shear Rate 1.00 1/s, Temperature 230 °C |
300000 cP @Shear Rate 1.00 1/s, Temperature 446 °F |
||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ISO 527-1/-2 |
| Elongation at Break | 12 % | 12 % | ISO 527-1/-2 |
| Elongation at Yield | 8.5 % | 8.5 % | ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.350 J/cm² @Temperature 23.0 °C |
1.67 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC60695-11-10 |
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
IEC60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 100 Hz |
0.0020 @Frequency 100 Hz |
IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4805 TPE, Transparent
- SGL Carbon Group SIGRAFIL C® C25 M350 UNS Milled Carbon Fiber, Unsized Carbon Fiber
- Total PSI 960E Polystyrene
- ChevronTexaco Transultex® CF H
- DayGlo Gem-Tone GC-18F Emerald Green
- ExxonMobil Enmist EP 220
- Eurostar Starpylen MH0200A HDPE, Injection Molding
- CPT C-Flex® R70-116 Opaque Biocompatible TPE
- ExxonMobil 625 Mobil SHC 600 Series
- BASF Neopor® 2200 Expandable Polystyrene
Copyright © lookpolymers.com All Rights Reserved