DSM Akulon® F136-E2 PA6
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Akulon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Akulon® F136-E2 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very High Viscosity, Lubricated, Nucleated, Film Extrusion
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Vapor Transmission | 35.0 g/m²/day @Temperature 23.0 °C |
2.25 g/100 in²/day @Temperature 73.4 °F |
at 85% r.h., film; DIS 15106-1/-3 |
| Oxygen Transmission | 1.15 cc-mm/m²-24hr-atm @Temperature 23.0 °C |
2.92 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F |
at 0% r.h., film; DIS 15105-1/-2 |
| 1.65 cc-mm/m²-24hr-atm @Temperature 23.0 °C |
4.19 cc-mil/100 in²-24hr-atm @Temperature 73.4 °F |
at 85% r.h., film; DIS 15105-1/-2 | |
| Viscosity | 2.25e+6 cP @Temperature 260 °C |
2.25e+6 cP @Temperature 500 °F |
Melt Viscosity; DSM method |
| 400000 cP @Shear Rate 1000 1/s, Temperature 240 °C |
400000 cP @Shear Rate 1000 1/s, Temperature 464 °F |
||
| 400000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
400000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
||
| 400000 cP @Shear Rate 1000 1/s, Temperature 280 °C |
400000 cP @Shear Rate 1000 1/s, Temperature 536 °F |
||
| 1.75e+6 cP @Shear Rate 0.100 1/s, Temperature 280 °C |
1.75e+6 cP @Shear Rate 0.100 1/s, Temperature 536 °F |
||
| 2.50e+6 cP @Shear Rate 0.100 1/s, Temperature 260 °C |
2.50e+6 cP @Shear Rate 0.100 1/s, Temperature 500 °F |
||
| 3.50e+6 cP @Shear Rate 0.100 1/s, Temperature 240 °C |
3.50e+6 cP @Shear Rate 0.100 1/s, Temperature 464 °F |
||
| Viscosity Measurement | 3.6 | 3.6 | RSV formic acid, 1g/100ml; DSM method |
| Viscosity Test | 245 cm³/g | 245 cm³/g | Viscosity Number; ISO 307, 1157, 1628 |
| Thickness | 50.0 microns | 1.97 mil | film |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 34.0 MPa | 4930 psi | parallel; ISO 527-3 |
| Film Elongation at Break, MD | 350 % | 350 % | parallel; ISO 527-3 |
| Modulus of Elasticity | 0.465 GPa | 67.4 ksi | film; DSM-Method, 50 mm/min |
| Coefficient of Friction, Dynamic | 0.80 | 0.80 | film; ISO 8295 |
| Coefficient of Friction, Static | 1.4 | 1.4 | film; ISO 8295 |
| Tear Strength Test | 32 | 32 | Trouser tear resistance, parallel, film; ISO 6383-1 |
| Film Tensile Strength at Break, MD | 94.0 MPa | 13600 psi | parallel; ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Specific Heat Capacity | 1.55 J/g-°C @Temperature 23.0 °C |
0.370 BTU/lb-°F @Temperature 73.4 °F |
|
| 2.25 J/g-°C @Temperature 20.0 - 150 °C |
0.538 BTU/lb-°F @Temperature 68.0 - 302 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 85 % | 85 % | film; DSM method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 °C | 518 °F | Extruder Temperature |
| Die Temperature | 270 °C | 518 °F | |
| Roll Temperature | 110 °C | 230 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Extrusion Type | Cast Film | |
| Puncture Resistance | 1320 J/m | Film (DSM Method) |
Users viewing this material also viewed the following:
- Nye Lubricants 786B (RL) Synthetic Oil
- Network Polymers Nylon 6040
- Process Technologies Inc Silicone/Metal Metal Detectable Sanitary Gasket
- Techmer ES HiFill® PA6 GF18 HS L 18% Glass Filled
- SABIC Innovative Plastics Ultem 1110V PEI (Asia Pacific)
- Samsung Cheil Industries Starex® WR-9120 J ASA, Unreinforced
- SABIC Innovative Plastics NORYL ENV150 PPE (Europe-Africa-Middle East)
- Axiall 14840 Wire & Cable Flexible PVC
- ChevronTexaco Rando® HD 46
Copyright © lookpolymers.com All Rights Reserved