Samsung Cheil Industries Infino® SC-1100R PC, Unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® SC-1100R PC, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
ASTM D570 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 63.7 MPa | 9250 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 97.1 MPa | 14100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 7.85 J/cm @Thickness 6.35 mm |
14.7 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 140 °C | 284 °F | B/50; ISO R306 |
| Flammability, UL94 | V-2 @Thickness 0.800 - 3.00 mm |
V-2 @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- MV Labs PB1000 PbSO4 Lead(II) sulfate
- Nilit Polynil® N66-P50N Lubed Nylon 6/6
- Solvay Specialty Polymers Udel® GF-110 Polysulfone (PSU) (Unverified Data**)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 91A
- Lucite International Lucite® 41 Acrylic Resin for Casting and Embedments
- Kostat E-3007J Conductive PS Compound
- Arlon R37053W007 0.007" (0.178 mm) Cured Silicone Rubber with Fiberglass Substrate
- ATI Allvac® Nickelvac® N-90 Nickel Superalloy, Heat Treatment: 1066°C (1950°F) + Age
- Beijing Chemical Industry KAIFA® MN-401 PA6 Resin
Copyright © lookpolymers.com All Rights Reserved