Covestro Bayblend® FR3010 IF PC/ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Covestro Bayblend® FR3010 IF PC/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injection molding• Increased heat resistanceAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	ISO 1183-1
Moisture Absorption at Equilibrium	0.20 %	0.20 %	ISO 62, 50% RH
Water Absorption at Saturation	0.50 %	0.50 %	ISO 62
Viscosity	210000 cP <br>@Shear Rate 1000 1/s,<br> Temperature 260 °C	210000 cP <br>@Shear Rate 1000 1/s,<br> Temperature 500 °F	melt viscosity; b.o. ISO 11443-A
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm <br>@Thickness 3.00 mm	0.0050 - 0.0070 in/in <br>@Thickness 0.118 in	150x105x3mm; b.o. ISO 2577
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm <br>@Thickness 3.00 mm	0.0050 - 0.0070 in/in <br>@Thickness 0.118 in	150x105x3mm; b.o. ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 MPa	7250 psi	50 mm/min; ISO 527-1,-2
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ISO 527-1,-2
Elongation at Break	>= 50 %	>= 50 %	50 mm/min; b.o. ISO 527-1,-2
Elongation at Yield	4.0 %	4.0 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	2.70 GPa	392 ksi	1 mm/min; ISO 527-1,-2
Izod Impact, Notched (ISO)	25.0 kJ/m² <br>@Temperature 23.0 °C	11.9 ft-lb/in² <br>@Temperature 73.4 °F	ISO 180-A
Izod Impact, Unnotched (ISO)	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	ISO 180-U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	76.0 µm/m-°C <br>@Temperature 23.0 - 55.0 °C	42.2 µin/in-°F <br>@Temperature 73.4 - 131 °F	ISO 11359-1,-2
CTE, linear, Transverse to Flow	80.0 µm/m-°C <br>@Temperature 23.0 - 55.0 °C	44.4 µin/in-°F <br>@Temperature 73.4 - 131 °F	ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi)	98.0 °C	208 °F	ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi)	88.0 °C	190 °F	ISO 75-1,-2
Vicat Softening Point	106 °C <br>@Load 5.10 kg	223 °F <br>@Load 11.2 lb	50°C/h; ISO 306
	108 °C <br>@Load 5.10 kg	226 °F <br>@Load 11.2 lb	120°C/h; ISO 306
Flammability, UL94	V-0 <br>@Thickness 1.50 mm	V-0 <br>@Thickness 0.0591 in
	5VB <br>@Thickness 2.20 mm	5VB <br>@Thickness 0.0866 in	UL 94-5V
	5VA <br>@Thickness 3.00 mm	5VA <br>@Thickness 0.118 in	UL 94-5V

Processing Properties	Metric	English	Comments
Melt Temperature	240 °C	464 °F	Injection molding; ISO 294
Mold Temperature	80.0 °C	176 °F	Injection molding; ISO 294
Injection Velocity	240 mm/sec	9.45 in/sec	ISO 294