Cossa Polimeri ESTAPROP K 0200 V2 Flame Retardant Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Extrusion Grade , Polypropylene, Flame Retardant
Manufacturer Cossa Polimeri S.r.L.
Trade Name ESTAPROP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cossa Polimeri ESTAPROP K 0200 V2 Flame Retardant Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PP copolymer extrusion gradeFlame retardant class V2, PBDE free, good impact strengthInformation provided by Cossa Polimeri S.r.l.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D 792
Linear Mold Shrinkage 0.015 - 0.018 cm/cm
0.015 - 0.018 in/in
ASTM D 955
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
ASTM D 638
Elongation at Break 70 %
70 %
ASTM D 638
Flexural Modulus 1.30 GPa
189 ksi
ASTM D 790
Izod Impact, Notched 0.250 J/cm

@Temperature -20.0 °C
 0.468 ft-lb/in

@Temperature -4.00 °F
 ASTM D 638
0.400 J/cm

@Temperature 0.000 °C
 0.749 ft-lb/in

@Temperature 32.0 °F
 ASTM D 638
0.800 J/cm

@Temperature 23.0 °C
 1.50 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
120°C/hr; ASTM D 648
Vicat Softening Point 147 °C

@Load 0.999 kg
 297 °F

@Load 2.20 lb
 50°C/hr; ASTM D 1525
Flammability, UL94 V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 I.E.C. 695-2-1