- Chosun Refractories SB90S Bricks, Oxide Bonded SiC
Chosun Refractories SB90S Bricks, Oxide Bonded SiC
| Category | Ceramic , Carbide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories SB90S Bricks, Oxide Bonded SiC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.65 g/cc | 0.0957 lb/in³ | |
| Porosity | 15 % | 15 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.02943 GPa @Temperature 250 °C |
4.269 ksi @Temperature 482 °F |
|
| 0.034335 GPa @Temperature 1400 °C |
4.9799 ksi @Temperature 2550 °F |
||
| Compressive Strength | 132 MPa | 19200 psi | Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.50 µm/m-°C @Temperature 1000 °C |
2.50 µin/in-°F @Temperature 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Fe2O3 | 0.40 % | 0.40 % | |
| SiC | 91 % | 91 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Refractories Under Load(2kg/?,T2?) | 1,700 |
Users viewing this material also viewed the following:
- Nye Lubricants 131A (DMO) Delicate Machinery Oil
- Nye Lubricants 760K (NG) Synthetic Oil
- LyondellBasell Petrothene® GA501021 Linear Low Density Polyethylene
- Industrial Laminates/Norplex NP320 Cotton Fabric
- Karina E 839-10/19-Y-CR White PVC Compound
- Styron Magnumâ„¢ 941 ABS
- EMS-Grivory Grivory® L 16 LM PA12
- DuPont Performance Polymers Zytel® 7304 NC010 Nylon 6 (Unverified Data**)
- Ascend Performance Materials Vydyne® 21SPG1 Nylon 66, DAM
- BASF Ultramid® B3UG4 LS BK 23215 20% Glass Filled PA66 FR (Dry)
Copyright © lookpolymers.com All Rights Reserved