- Cossa Polimeri ESTAPROP H 0560 GF Polypropylene, 30% Glass Filled
Cossa Polimeri ESTAPROP H 0560 GF Polypropylene, 30% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP H 0560 GF Polypropylene, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP homopolymer 30% glass fiber reinforcedGood physical and mechanical characteristicsInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D 955 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
| Tensile Modulus | 6.50 GPa | 943 ksi | ASTM D 638 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.300 J/cm @Temperature -20.0 °C |
0.562 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| 0.500 J/cm @Temperature 0.000 °C |
0.937 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
| 0.600 J/cm @Temperature 23.0 °C |
1.12 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 120 °C @Load 5.00 kg |
248 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- Okulen® 1000 PE-UHMW, MoS2 -Moly-
- Precision Polymer Engineering N70X Nitrile Rubber
- SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific)
- Pau Tai UNISTAB CS-905 Liquid Stabilizer for Paste Resin
- Solvay Specialty Polymers Udel® P-1700 Polysulfone (PSU) (Unverified Data**)
- SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA
- Tipco Tipcofil® AG 200 - 10% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
- DuPont™ Nomex® 411 Paper, 7 mil Nominal Thickness
- Denka REOMER G G8070 Thermoplastic Elastomer, For Injection Molding
Copyright © lookpolymers.com All Rights Reserved