Cossa Polimeri ESTADIENE 1050 AS Acrylonitrile Butadiene Styrene
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 1050 AS Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose ABSGood impact resistance, high melt flow rate, high gloss, with antistatic, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 50 g/10 min @Load 10.0 kg, Temperature 220 °C |
50 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ASTM D 638 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D 638 |
| Elongation at Break | 12 % | 12 % | ASTM D 638 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 0.000 °C |
1.50 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 103 °C @Load 0.999 kg |
217 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Huntsman Araldite GT 6084 Bisphenol A Epoxy Solid Resin
- IRPC Polimaxx Polene G2855 High Density Polyethylene
- Lubriplate 777 NO. Specialty Lubricant and Grease
- Kraton® D4433 P (O/E SIS) Linear Triblock Copolymer
- Menzolit Menzolit® SMC 0190 Unsaturated Polyester UP
- Johnson Matthey JM6236 Soft Solder/Flux
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- Diamond Polymers ABS 3002MC
- Chosun Refractories GUN-120L Light-Weight Gunning Castable
- Ceradyne SEMICORE® S2-17A MMPA 24/18 Sm2 (CoFeCuZr)17 Samarium Cobalt Magnet
Copyright © lookpolymers.com All Rights Reserved