| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTADIENE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTADIENE 1020 HHT Acrylonitrile Butadiene Styrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS with very high heat resistanceGood melt flow rate, good impact resistance, stiff, excellent surface appearance, good processabilityInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D 955 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ASTM D 638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ASTM D 638 |
| Elongation at Break | 20 % | 20 % | ASTM D 638 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.50 J/cm @Temperature 0.000 °C |
2.81 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 |
| 2.00 J/cm @Temperature 23.0 °C |
3.75 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 112 °C @Load 5.00 kg |
234 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| 120 °C @Load 0.999 kg |
248 °F @Load 2.20 lb |
50°C/hr; ASTM D 1525 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
I.E.C. 695-2-1 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8512G (842G) (UF) Synthetic Oil
- Nabaltec NABALOX® NO 113 Ground Alumina
- Reliance Industries Polypropylene Random Copolymer
- Styron Magnumâ„¢ 2630 ABS, High Impact
- Constellium PLAN 5754 Aluminum Rolled Plate
- Eastman Tenite Butyrate 285A2R30023 Natural, Trsp Cellulose Acetate Butyrate
- ELASTO UK Dryflex® 660350S SEBS Based Material, Semi-Filled Qualities, 35A Hardness, Natural
- BASF Paliogen® Red L 4120 Color Additive
- BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved