Cossa Polimeri ESTADIENE 1016 HT V0 Flame Retardant ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTADIENE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cossa Polimeri ESTADIENE 1016 HT V0 Flame Retardant ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Acrylonitrile Butadiene StyreneFlame retardant class V0, with PBDE, high thermal resistance, good physical and mechanical characteristics, excellent processabilityInformation provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ASTM D 792
Linear Mold Shrinkage	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in	ASTM D 955
Melt Flow	4.0 g/10 min @Load 10.0 kg, Temperature 220 °C	4.0 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D 1238
	14 g/10 min @Load 5.00 kg, Temperature 240 °C	14 g/10 min @Load 11.0 lb, Temperature 464 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	43.0 MPa	6240 psi	ASTM D 638
Tensile Strength, Yield	50.0 MPa	7250 psi	ASTM D 638
Elongation at Break	5.0 %	5.0 %	ASTM D 638
Flexural Modulus	2.70 GPa	392 ksi	ASTM D 790
Izod Impact, Notched	0.700 J/cm @Temperature 0.000 °C	1.31 ft-lb/in @Temperature 32.0 °F	ASTM D 638
	0.900 J/cm @Temperature 23.0 °C	1.69 ft-lb/in @Temperature 73.4 °F	ASTM D 256

Thermal Properties	Metric	English	Comments
Hot Ball Pressure Test	105 °C	221 °F	I.E.C. 335-1
Vicat Softening Point	115 °C @Load 5.00 kg	239 °F @Load 11.0 lb	50°C/hr; ASTM D 1525
	123 °C @Load 0.999 kg	253 °F @Load 2.20 lb	50°C/hr; ASTM D 1525
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Glow Wire Test	960 °C	1760 °F	I.E.C. 695-2-1