Cossa Polimeri ESTABLEND PA 1424 GF HI ABS / Nylon 6 Blend, 12% Glass Filled

Category	Polymer , Thermoplastic , ABS Polymer , Nylon , Nylon 6
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTABLEND PA
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cossa Polimeri ESTABLEND PA 1424 GF HI ABS / Nylon 6 Blend, 12% Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.12% glass fiber reinforcedHigh impact strength, high chemical resistance, excellent heat resistance, high dimensional stability, low shrinkageInformation provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in	ISO 2577
Melt Flow	14 g/10 min @Load 10.0 kg, Temperature 240 °C	14 g/10 min @Load 22.0 lb, Temperature 464 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	52.0 MPa	7540 psi	ISO 527
Elongation at Break	3.0 %	3.0 %	ISO 527
Tensile Modulus	3.80 GPa	551 ksi	ISO 527
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Izod Impact, Notched	0.100 J/cm @Temperature 23.0 °C	0.187 ft-lb/in @Temperature 73.4 °F	ISO 180/A

Thermal Properties	Metric	English	Comments
Vicat Softening Point	109 °C @Load 5.00 kg	228 °F @Load 11.0 lb	50°C/hr; ISO 306
	185 °C @Load 0.999 kg	365 °F @Load 2.20 lb	50°C/hr; ISO 306
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in