Constellium Certal® SPC Aluminum

Category	Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy
Manufacturer	Constellium
Trade Name	Certal®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Constellium Certal® SPC Aluminum.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Certal® SPC has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important property in many types of applications. Typical applications include compression or injection moulds for plastics.Information provided by manufacturer

Physical Properties	Metric	English	Comments
Density	2.76 g/cc	0.0997 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	140 @Thickness 240 - 305 mm	140 @Thickness 9.45 - 12.0 in
	160 @Thickness 150 - 240 mm	160 @Thickness 5.91 - 9.45 in
Tensile Strength	>= 490 MPa @Thickness 240 - 305 mm	>= 71100 psi @Thickness 9.45 - 12.0 in	Tempers T651 / T652
	>= 510 MPa @Thickness 150 - 240 mm	>= 74000 psi @Thickness 5.91 - 9.45 in	Tempers T651 / T652
	520 MPa @Thickness 240 - 305 mm	75400 psi @Thickness 9.45 - 12.0 in	Tempers T651 / T652
	530 MPa @Thickness 150 - 240 mm	76900 psi @Thickness 5.91 - 9.45 in	Tempers T651 / T652
Tensile Strength, Yield	>= 430 MPa @Strain 0.200 %, Thickness 240 - 305 mm	>= 62400 psi @Strain 0.200 %, Thickness 9.45 - 12.0 in	Tempers T651 / T652
	>= 440 MPa @Strain 0.200 %, Thickness 150 - 240 mm	>= 63800 psi @Strain 0.200 %, Thickness 5.91 - 9.45 in	Tempers T651 / T652
	450 MPa @Strain 0.200 %, Thickness 240 - 305 mm	65300 psi @Strain 0.200 %, Thickness 9.45 - 12.0 in	Typical Strength
	460 MPa @Strain 0.200 %, Thickness 150 - 240 mm	66700 psi @Strain 0.200 %, Thickness 5.91 - 9.45 in	Typical Strength
Elongation at Break	>= 2.0 % @Thickness 240 - 305 mm	>= 2.0 % @Thickness 9.45 - 12.0 in	Tempers T651 / T652
	>= 4.0 % @Thickness 150 - 240 mm	>= 4.0 % @Thickness 5.91 - 9.45 in	Tempers T651 / T652
	5.0 % @Thickness 240 - 305 mm	5.0 % @Thickness 9.45 - 12.0 in	Typical Elongation
	7.0 % @Thickness 150 - 240 mm	7.0 % @Thickness 5.91 - 9.45 in	Typical Elongation
Modulus of Elasticity	72.0 GPa	10400 ksi	tensile
	73.0 GPa	10600 ksi	compression

Thermal Properties	Metric	English
CTE, linear	23.6 µm/m-°C @Temperature 20.0 - 100 °C	13.1 µin/in-°F @Temperature 68.0 - 212 °F
Specific Heat Capacity	0.873 J/g-°C	0.209 BTU/lb-°F
Thermal Conductivity	150 W/m-K	1040 BTU-in/hr-ft²-°F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	88.9 - 92.45 %	88.9 - 92.45 %	as balance
Chromium, Cr	<= 0.10 %	<= 0.10 %
Copper, Cu	0.50 - 1.0 %	0.50 - 1.0 %
Iron, Fe	<= 0.35 %	<= 0.35 %
Magnesium, Mg	2.6 - 3.7 %	2.6 - 3.7 %
Manganese, Mn	<= 0.10 %	<= 0.10 %
Silicon, Si	<= 0.25 %	<= 0.25 %
Titanium, Ti	<= 0.15 %	<= 0.15 %
Zinc, Zn	4.3 - 5.2 %	4.3 - 5.2 %
Zirconium, Zr	0.15 - 0.25 %	0.15 - 0.25 %