Material Notes:
The Alumold®-400 alloy has been optimized to provide good shape stability and high strength properties throughout the plate thickness. Typical applications include blow moulds, thermoforming moulds and injection moulds for small series.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.79 g/cc
0.101 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 120

@Thickness 254 - 305 mm
 120

@Thickness 10.0 - 12.0 in
125

@Thickness 152.4 - 203.2 mm
 125

@Thickness 6.000 - 8.000 in
125

@Thickness 203.2 - 254 mm
 125

@Thickness 8.000 - 10.0 in
130

@Thickness 38.1 - 76.2 mm
 130

@Thickness 1.50 - 3.00 in
130

@Thickness 76.2 - 127 mm
 130

@Thickness 3.00 - 5.00 in
130

@Thickness 127 - 152.4 mm
 130

@Thickness 5.00 - 6.000 in
140

@Thickness 15.0 - 38.1 mm
 140

@Thickness 0.591 - 1.50 in
Tensile Strength >= 390 MPa

@Thickness 203.2 - 254 mm
 >= 56600 psi

@Thickness 8.000 - 10.0 in
 Tempers T651 / T652
>= 395 MPa

@Thickness 152.4 - 203.2 mm
 >= 57300 psi

@Thickness 6.000 - 8.000 in
 Tempers T651 / T652
>= 400 MPa

@Thickness 127 - 152.4 mm
 >= 58000 psi

@Thickness 5.00 - 6.000 in
 Tempers T651 / T652
400 MPa

@Thickness 254 - 305 mm
 58000 psi

@Thickness 10.0 - 12.0 in
 Typical Strength
>= 415 MPa

@Thickness 38.1 - 76.2 mm
 >= 60200 psi

@Thickness 1.50 - 3.00 in
 Tempers T651 / T652
>= 415 MPa

@Thickness 76.2 - 127 mm
 >= 60200 psi

@Thickness 3.00 - 5.00 in
 Tempers T651 / T652
420 MPa

@Thickness 203.2 - 254 mm
 60900 psi

@Thickness 8.000 - 10.0 in
 Typical Strength
425 MPa

@Thickness 152.4 - 203.2 mm
 61600 psi

@Thickness 6.000 - 8.000 in
 Typical Strength
>= 425 MPa

@Thickness 15.0 - 38.1 mm
 >= 61600 psi

@Thickness 0.591 - 1.50 in
 Tempers T651 / T652
430 MPa

@Thickness 127 - 152.4 mm
 62400 psi

@Thickness 5.00 - 6.000 in
 Typical Strength
440 MPa

@Thickness 38.1 - 76.2 mm
 63800 psi

@Thickness 1.50 - 3.00 in
 Typical Strength
440 MPa

@Thickness 76.2 - 127 mm
 63800 psi

@Thickness 3.00 - 5.00 in
 Typical Strength
450 MPa

@Thickness 15.0 - 38.1 mm
 65300 psi

@Thickness 0.591 - 1.50 in
 Typical Strength
Tensile Strength, Yield >= 330 MPa

@Strain 0.200 %,
Thickness 203.2 - 254 mm
 >= 47900 psi

@Strain 0.200 %,
Thickness 8.000 - 10.0 in
 Tempers T651 / T652
>= 340 MPa

@Strain 0.200 %,
Thickness 152.4 - 203.2 mm
 >= 49300 psi

@Strain 0.200 %,
Thickness 6.000 - 8.000 in
 Tempers T651 / T652
340 MPa

@Strain 0.200 %,
Thickness 254 - 305 mm
 49300 psi

@Strain 0.200 %,
Thickness 10.0 - 12.0 in
 Typical Strength
>= 350 MPa

@Strain 0.200 %,
Thickness 127 - 152.4 mm
 >= 50800 psi

@Strain 0.200 %,
Thickness 5.00 - 6.000 in
 Tempers T651 / T652
360 MPa

@Strain 0.200 %,
Thickness 203.2 - 254 mm
 52200 psi

@Strain 0.200 %,
Thickness 8.000 - 10.0 in
 Typical Strength
370 MPa

@Strain 0.200 %,
Thickness 152.4 - 203.2 mm
 53700 psi

@Strain 0.200 %,
Thickness 6.000 - 8.000 in
 Typical Strength
>= 370 MPa

@Strain 0.200 %,
Thickness 38.1 - 76.2 mm
 >= 53700 psi

@Strain 0.200 %,
Thickness 1.50 - 3.00 in
 Tempers T651 / T652
>= 370 MPa

@Strain 0.200 %,
Thickness 76.2 - 127 mm
 >= 53700 psi

@Strain 0.200 %,
Thickness 3.00 - 5.00 in
 Tempers T651 / T652
>= 380 MPa

@Strain 0.200 %,
Thickness 15.0 - 38.1 mm
 >= 55100 psi

@Strain 0.200 %,
Thickness 0.591 - 1.50 in
 Tempers T651 / T652
380 MPa

@Strain 0.200 %,
Thickness 127 - 152.4 mm
 55100 psi

@Strain 0.200 %,
Thickness 5.00 - 6.000 in
 Typical Strength
395 MPa

@Strain 0.200 %,
Thickness 38.1 - 76.2 mm
 57300 psi

@Strain 0.200 %,
Thickness 1.50 - 3.00 in
 Typical Strength
395 MPa

@Strain 0.200 %,
Thickness 76.2 - 127 mm
 57300 psi

@Strain 0.200 %,
Thickness 3.00 - 5.00 in
 Typical Strength
410 MPa

@Strain 0.200 %,
Thickness 15.0 - 38.1 mm
 59500 psi

@Strain 0.200 %,
Thickness 0.591 - 1.50 in
 Typical Strength
Elongation at Break 5.0 %

@Thickness 254 - 305 mm
 5.0 %

@Thickness 10.0 - 12.0 in
 Typical Elongation
>= 5.0 %

@Thickness 203.2 - 254 mm
 >= 5.0 %

@Thickness 8.000 - 10.0 in
 Tempers T651 / T652
>= 6.0 %

@Thickness 152.4 - 203.2 mm
 >= 6.0 %

@Thickness 6.000 - 8.000 in
 Tempers T651 / T652
>= 7.0 %

@Thickness 76.2 - 127 mm
 >= 7.0 %

@Thickness 3.00 - 5.00 in
 Tempers T651 / T652
>= 7.0 %

@Thickness 127 - 152.4 mm
 >= 7.0 %

@Thickness 5.00 - 6.000 in
 Tempers T651 / T652
>= 8.0 %

@Thickness 38.1 - 76.2 mm
 >= 8.0 %

@Thickness 1.50 - 3.00 in
 Tempers T651 / T652
>= 9.0 %

@Thickness 15.0 - 38.1 mm
 >= 9.0 %

@Thickness 0.591 - 1.50 in
 Tempers T651 / T652
9.0 %

@Thickness 152.4 - 203.2 mm
 9.0 %

@Thickness 6.000 - 8.000 in
 Typical Elongation
9.0 %

@Thickness 203.2 - 254 mm
 9.0 %

@Thickness 8.000 - 10.0 in
 Typical Elongation
10 %

@Thickness 76.2 - 127 mm
 10 %

@Thickness 3.00 - 5.00 in
 Typical Elongation
10 %

@Thickness 127 - 152.4 mm
 10 %

@Thickness 5.00 - 6.000 in
 Typical Elongation
11 %

@Thickness 38.1 - 76.2 mm
 11 %

@Thickness 1.50 - 3.00 in
 Typical Elongation
12 %

@Thickness 15.0 - 38.1 mm
 12 %

@Thickness 0.591 - 1.50 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
tensile
73.0 GPa
10600 ksi
compression
Thermal Properties Metric English Comments
CTE, linear 23.5 µm/m-°C

@Temperature 20.0 - 100 °C
 13.1 µin/in-°F

@Temperature 68.0 - 212 °F
Specific Heat Capacity 0.960 J/g-°C
0.229 BTU/lb-°F
Thermal Conductivity 122 W/m-K
847 BTU-in/hr-ft²-°F
Descriptive Properties Value Comments
Thermal Diffusivity 45.5 mm²/s
Users viewing this material also viewed the following: