Constellium Alumold® 350 Aluminum

Category Metal , Nonferrous Metal , Aluminum Alloy , 5000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name Alumold®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Constellium Alumold® 350 Aluminum.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Alumold-350® has been specifically developed to achieve the best combination of strength at low and high temperatures, together with a good shape stability and machinability. Alumold-350® is particularly suitable for plastic forming machinery operating at temperatures up to 200°C, which is the temperature for molding of rubber and other elastomers.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.84 g/cc
0.103 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 110
<br>@Thickness 254 - 305 mm
 110
<br>@Thickness 10.0 - 12.0 in
120
<br>@Thickness 203.2 - 254 mm
 120
<br>@Thickness 8.000 - 10.0 in
125
<br>@Thickness 152.4 - 203.2 mm
 125
<br>@Thickness 6.000 - 8.000 in
135
<br>@Thickness 127 - 152.4 mm
 135
<br>@Thickness 5.00 - 6.000 in
140
<br>@Thickness 101.6 - 127 mm
 140
<br>@Thickness 4.000 - 5.00 in
145
<br>@Thickness 7.90 - 50.8 mm
 145
<br>@Thickness 0.311 - 2.00 in
145
<br>@Thickness 50.8 - 76.2 mm
 145
<br>@Thickness 2.00 - 3.00 in
145
<br>@Thickness 76.2 - 101.6 mm
 145
<br>@Thickness 3.00 - 4.000 in
Tensile Strength >= 320 MPa
<br>@Thickness 254 - 305 mm
 >= 46400 psi
<br>@Thickness 10.0 - 12.0 in
 Tempers T851/T852)
>= 355 MPa
<br>@Thickness 203.2 - 254 mm
 >= 51500 psi
<br>@Thickness 8.000 - 10.0 in
 Tempers T851/T852)
360 MPa
<br>@Thickness 254 - 305 mm
 52200 psi
<br>@Thickness 10.0 - 12.0 in
 Typical Strength
>= 380 MPa
<br>@Thickness 152.4 - 203.2 mm
 >= 55100 psi
<br>@Thickness 6.000 - 8.000 in
 Tempers T851/T852)
390 MPa
<br>@Thickness 203.2 - 254 mm
 56600 psi
<br>@Thickness 8.000 - 10.0 in
 Typical Strength
>= 393 MPa
<br>@Thickness 127 - 152.4 mm
 >= 57000 psi
<br>@Thickness 5.00 - 6.000 in
 Tempers T851/T852)
>= 407 MPa
<br>@Thickness 101.6 - 127 mm
 >= 59000 psi
<br>@Thickness 4.000 - 5.00 in
 Tempers T851/T852)
>= 414 MPa
<br>@Thickness 76.2 - 101.6 mm
 >= 60000 psi
<br>@Thickness 3.00 - 4.000 in
 Tempers T851/T852)
420 MPa
<br>@Thickness 152.4 - 203.2 mm
 60900 psi
<br>@Thickness 6.000 - 8.000 in
 Typical Strength
>= 428 MPa
<br>@Thickness 7.90 - 50.8 mm
 >= 62100 psi
<br>@Thickness 0.311 - 2.00 in
 Tempers T851/T852)
>= 428 MPa
<br>@Thickness 50.8 - 76.2 mm
 >= 62100 psi
<br>@Thickness 2.00 - 3.00 in
 Tempers T851/T852)
455 MPa
<br>@Thickness 127 - 152.4 mm
 66000 psi
<br>@Thickness 5.00 - 6.000 in
 Typical Strength
465 MPa
<br>@Thickness 7.90 - 50.8 mm
 67400 psi
<br>@Thickness 0.311 - 2.00 in
 Typical Strength
465 MPa
<br>@Thickness 50.8 - 76.2 mm
 67400 psi
<br>@Thickness 2.00 - 3.00 in
 Typical Strength
465 MPa
<br>@Thickness 76.2 - 101.6 mm
 67400 psi
<br>@Thickness 3.00 - 4.000 in
 Typical Strength
480 MPa
<br>@Thickness 101.6 - 127 mm
 69600 psi
<br>@Thickness 4.000 - 5.00 in
 Typical Strength
Tensile Strength, Yield >= 240 MPa
<br>@Strain 0.200 %,<br> Thickness 254 - 305 mm
 >= 34800 psi
<br>@Strain 0.200 %,<br> Thickness 10.0 - 12.0 in
 Tempers T851/T852
>= 270 MPa
<br>@Strain 0.200 %,<br> Thickness 203.2 - 254 mm
 >= 39200 psi
<br>@Strain 0.200 %,<br> Thickness 8.000 - 10.0 in
 Tempers T851/T852
>= 280 MPa
<br>@Strain 0.200 %,<br> Thickness 152.4 - 203.2 mm
 >= 40600 psi
<br>@Strain 0.200 %,<br> Thickness 6.000 - 8.000 in
 Tempers T851/T852
>= 290 MPa
<br>@Strain 0.200 %,<br> Thickness 127 - 152.4 mm
 >= 42100 psi
<br>@Strain 0.200 %,<br> Thickness 5.00 - 6.000 in
 Tempers T851/T852
>= 297 MPa
<br>@Strain 0.200 %,<br> Thickness 101.6 - 127 mm
 >= 43100 psi
<br>@Strain 0.200 %,<br> Thickness 4.000 - 5.00 in
 Tempers T851/T852
>= 304 MPa
<br>@Strain 0.200 %,<br> Thickness 76.2 - 101.6 mm
 >= 44100 psi
<br>@Strain 0.200 %,<br> Thickness 3.00 - 4.000 in
 Tempers T851/T852
>= 310 MPa
<br>@Strain 0.200 %,<br> Thickness 50.8 - 76.2 mm
 >= 45000 psi
<br>@Strain 0.200 %,<br> Thickness 2.00 - 3.00 in
 Tempers T851/T852
310 MPa
<br>@Strain 0.200 %,<br> Thickness 254 - 305 mm
 45000 psi
<br>@Strain 0.200 %,<br> Thickness 10.0 - 12.0 in
 Typical Strength
315 MPa
<br>@Strain 0.200 %,<br> Thickness 203.2 - 254 mm
 45700 psi
<br>@Strain 0.200 %,<br> Thickness 8.000 - 10.0 in
 Typical Strength
>= 317 MPa
<br>@Strain 0.200 %,<br> Thickness 7.90 - 50.8 mm
 >= 46000 psi
<br>@Strain 0.200 %,<br> Thickness 0.311 - 2.00 in
 Tempers T851/T852
330 MPa
<br>@Strain 0.200 %,<br> Thickness 152.4 - 203.2 mm
 47900 psi
<br>@Strain 0.200 %,<br> Thickness 6.000 - 8.000 in
 Typical Strength
360 MPa
<br>@Strain 0.200 %,<br> Thickness 127 - 152.4 mm
 52200 psi
<br>@Strain 0.200 %,<br> Thickness 5.00 - 6.000 in
 Typical Strength
365 MPa
<br>@Strain 0.200 %,<br> Thickness 101.6 - 127 mm
 52900 psi
<br>@Strain 0.200 %,<br> Thickness 4.000 - 5.00 in
 Typical Strength
366 MPa
<br>@Strain 0.200 %,<br> Thickness 7.90 - 50.8 mm
 53100 psi
<br>@Strain 0.200 %,<br> Thickness 0.311 - 2.00 in
 Typical Strength
366 MPa
<br>@Strain 0.200 %,<br> Thickness 50.8 - 76.2 mm
 53100 psi
<br>@Strain 0.200 %,<br> Thickness 2.00 - 3.00 in
 Typical Strength
366 MPa
<br>@Strain 0.200 %,<br> Thickness 76.2 - 101.6 mm
 53100 psi
<br>@Strain 0.200 %,<br> Thickness 3.00 - 4.000 in
 Typical Strength
Elongation at Break >= 0.50 %
<br>@Thickness 254 - 305 mm
 >= 0.50 %
<br>@Thickness 10.0 - 12.0 in
 Tempers T851/T852)
>= 1.0 %
<br>@Thickness 203.2 - 254 mm
 >= 1.0 %
<br>@Thickness 8.000 - 10.0 in
 Tempers T851/T852)
>= 2.0 %
<br>@Thickness 152.4 - 203.2 mm
 >= 2.0 %
<br>@Thickness 6.000 - 8.000 in
 Tempers T851/T852)
2.0 %
<br>@Thickness 254 - 305 mm
 2.0 %
<br>@Thickness 10.0 - 12.0 in
 Typical Elongation
3.0 %
<br>@Thickness 203.2 - 254 mm
 3.0 %
<br>@Thickness 8.000 - 10.0 in
 Typical Elongation
4.0 %
<br>@Thickness 152.4 - 203.2 mm
 4.0 %
<br>@Thickness 6.000 - 8.000 in
 Typical Elongation
>= 4.0 %
<br>@Thickness 127 - 152.4 mm
 >= 4.0 %
<br>@Thickness 5.00 - 6.000 in
 Tempers T851/T852)
>= 5.0 %
<br>@Thickness 76.2 - 101.6 mm
 >= 5.0 %
<br>@Thickness 3.00 - 4.000 in
 Tempers T851/T852)
>= 5.0 %
<br>@Thickness 101.6 - 127 mm
 >= 5.0 %
<br>@Thickness 4.000 - 5.00 in
 Tempers T851/T852)
6.0 %
<br>@Thickness 127 - 152.4 mm
 6.0 %
<br>@Thickness 5.00 - 6.000 in
 Typical Elongation
>= 6.0 %
<br>@Thickness 50.8 - 76.2 mm
 >= 6.0 %
<br>@Thickness 2.00 - 3.00 in
 Tempers T851/T852)
>= 7.0 %
<br>@Thickness 7.90 - 50.8 mm
 >= 7.0 %
<br>@Thickness 0.311 - 2.00 in
 Tempers T851/T852)
7.0 %
<br>@Thickness 101.6 - 127 mm
 7.0 %
<br>@Thickness 4.000 - 5.00 in
 Typical Elongation
8.0 %
<br>@Thickness 76.2 - 101.6 mm
 8.0 %
<br>@Thickness 3.00 - 4.000 in
 Typical Elongation
9.0 %
<br>@Thickness 7.90 - 50.8 mm
 9.0 %
<br>@Thickness 0.311 - 2.00 in
 Typical Elongation
9.0 %
<br>@Thickness 50.8 - 76.2 mm
 9.0 %
<br>@Thickness 2.00 - 3.00 in
 Typical Elongation
Modulus of Elasticity 72.4 GPa
10500 ksi
Thermal Properties Metric English Comments
CTE, linear 22.3 µm/m-°C
<br>@Temperature 20.0 - 100 °C
 12.4 µin/in-°F
<br>@Temperature 68.0 - 212 °F
Thermal Conductivity 130 W/m-K
902 BTU-in/hr-ft²-°F
Temper T851
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000550 ohm-cm
0.00000550 ohm-cm
Temper T851