Clariant Renol PPSP0017 Polypropylene, Static Dissipative
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPSP0017 Polypropylene, Static Dissipative.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Temperature 22.8 °C |
5.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 - 1.00e+7 ohm-cm | 1e+05 - 1.00e+7 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 221 °C | 380 - 430 °F | |
| Mold Temperature | 21.1 - 37.8 °C | 70.0 - 100 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture level is less than 0.10% |
| Injection Pressure | 41.4 - 74.5 MPa | 6000 - 10800 psi | Secondary |
| 68.9 - 103 MPa | 10000 - 15000 psi | Initial | |
| Back Pressure | 1.38 - 1.72 MPa | 200 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hybrid S459HTP ABS + Polycarbonate Alloy
- Gromax PBT 5130-104 30% Glass Fiber Filled
- Lanxess Pocan® KL 1-7033 000000 PBT, 30% Glass Fiber
- H.C. Starck Grade HD 07 Boron Carbide, B4C
- Saint-Gobain CHR® HM426 High Modulus PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Lubrizol Estane® S392A Thermoplastic Polyurethane
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plastolein 9057 Plasticizer
- Dow Corning 808 RESIN
- Ascend Performance Materials Vydyne® R220/R228 Nylon 66, 40% Mineral Reinforced, Conditioned (2.5% Moisture)
- 3M Scotch® 898MSR Filament Tape
Copyright © lookpolymers.com All Rights Reserved