Techmer ES Electrafil® J-1/CF/40 NAT PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-1/CF/40 NAT PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 Hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 276 MPa | 40000 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 407 MPa | 59000 psi | ASTM D790 |
| Flexural Modulus | 23.4 GPa | 3400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 °C |
8.00 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 10 ohm-cm | 1.0 - 10 ohm-cm | ASTM D648 |
| Surface Resistivity per Square | 10 - 100 ohm | 10 - 100 ohm | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Shielding @ 1 GHz | 30-40 db | ES7-83 |
Users viewing this material also viewed the following:
- NYCOA 1417 HS Heat Stabilized, Impact Modified Nylon 6 Resin
- Techmer ES Plastiblend® PA6/6,6 109 L Nylon 6/66
- Teknor Apex Synres® PP 70 MH13 MB Polypropylene
- Total PPH 3576 H Polypropylene Homopolymer, Cast Film
- A. Schulman POLYBATCH™ Red 502 Concentrate Based In Polyethylene
- Hexcel® HexForce™ SA047 Fiber Glass Fabric
- E-Polymers TEKANATE® G7020 General Purpose Easy Molding Polycarbonate
- Akro-Plastic Akromid® B3 GF 30 S1 BLACK (1281) PA, Cold-Impact Resistant, 30% Glass Filled, Black
Copyright © lookpolymers.com All Rights Reserved