Clariant Renol PEEKSP0002 Polyetheretherketone, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PEEKSP0002 Polyetheretherketone, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 179 MPa | 26000 psi | ASTM D638 |
| Flexural Yield Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C |
1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 349 - 399 °C | 660 - 750 °F | |
| Mold Temperature | 163 - 218 °C | 325 - 425 °F | |
| Dry Time | <= 3 hour @Temperature 149 °C |
<= 3 hour @Temperature 300 °F |
to ensure moisture level is below 0.1% |
| Injection Pressure | 49.6 - 74.5 MPa | 7200 - 10800 psi | Secondary |
| 82.7 - 124 MPa | 12000 - 18000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm |
Users viewing this material also viewed the following:
- Permabond 919 Cyanoacrylate, High temperature
- LG Chemical LUPOY HI1002ML PC, High Impact
- Isoflon PTFE + 3% MoS2 Polytetrafluoroethylene with 3% Molybdenum disulfide
- A. Schulman POLYBATCH™ Yellow 2450E Concentrate Based In Polyethylene
- Lubrizol ESTANE® 58888 Ether Based Thermoplastic Polyurethane (European Grade)
- Diamond Polymers Centrex® 885 Profile Extrusion Grade
- BASF Ultramid® 1403-2 BK ND3007 PA66 (Dry)
- Solvay RHODAPHOSE® TBP-HP Phosphorus Derivative
Copyright © lookpolymers.com All Rights Reserved