Chevron Phillips MarFlex® 7105FL Polyethylene; LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips MarFlex® 7105FL Polyethylene; LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: High strengthGood drawdownGood processabilityUse alone or in blends with LDPE or HDPEHigh amounts of slip and antiblocking agents Applications: Typical blown film applications include: Industrial linersHeavy duty bagsInstitutional packagingInformation provided by Phillips

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ASTM D-1505
Melt Index of Compound	0.50 g/10 min @Load 2.16 kg, Temperature 190 °C	0.50 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D-1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	540 %	540 %	Blown Film at 1 mil; ASTM D-882
Film Elongation at Break, TD	580 %	580 %	Blown Film at 1 mil; ASTM D-882
Coefficient of Friction	0.10	0.10	Blown Film at 1 mil; ASTM D-1894
Elmendorf Tear Strength, MD	15.7 g/micron	400 g/mil	Blown Film at 1 mil; ASTM D-1922
Elmendorf Tear Strength, TD	21.7 g/micron	550 g/mil	Blown Film at 1 mil; ASTM D-1922
Dart Drop	15.7 g/micron	400 g/mil	Blown Film at 1 mil; ASTM D-1709
Film Tensile Strength at Break, MD	36.0 MPa	5220 psi	Blown Film at 1 mil; ASTM D-882
Film Tensile Strength at Break, TD	34.0 MPa	4930 psi	Blown Film at 1 mil; ASTM D-882
1% Secant Modulus, MD	200 MPa	29000 psi	Blown Film at 1 mil; ASTM D-882
1% Secant Modulus, TD	214 MPa	31000 psi	Blown Film at 1 mil; ASTM D-882

Optical Properties	Metric	English	Comments
Haze	14 %	14 %	Blown Film at 1 mil; ASTM D-1003
Gloss	80 %	80 %	60°, Blown Film at 1 mil; ASTM D-2457

Descriptive Properties	Value	Comments
Process Aid	Yes