Chevron Phillips MC3650 Crystal Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Transparent Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips MC3650 Crystal Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

General purpose crystal polystyrene.Applications:HousewaresConsumer containers, vials, jars, etc.Disposable cutleryInjection molded drink cupsFeatures:Easy filling of thin-walled partsExceptional mold releaseExcellent clarity with slight blue tintImproved cycle times in hard to fill partsGood toughnessInformation provided by Chevron PhillipsThe Chevron Phillips polystyrene product line was transferred to Americas Styrenics in 2008.

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D-792
Bulk Density	0.609 - 0.673 g/cc	0.0220 - 0.0243 lb/in³
Linear Mold Shrinkage	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	24 hours; ASTM D-955
Melt Flow	13 g/10 min @Load 5.00 kg, Temperature 200 °C	13 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D-1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	47.0 MPa	6820 psi	0.2 in/min; 0.125" thickness; ASTM D-638
Elongation at Yield	3.0 %	3.0 %	0.2 in/min; 0.125" thickness; ASTM D-638
Tensile Modulus	3.10 GPa	450 ksi	0.2 in/min; 0.125" thickness; ASTM D-638
Flexural Strength	62.0 MPa	8990 psi	0.1 in/min; 0.250" thickness; ASTM D-790B
Flexural Modulus	3.10 GPa	450 ksi	0.1 in/min; 0.250" thickness; ASTM D-790B
Izod Impact, Notched	0.190 J/cm @Thickness 3.17 mm, Temperature 22.8 °C	0.356 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F	ASTM D-256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	82.0 °C @Thickness 6.35 mm	180 °F @Thickness 0.250 in	ASTM D-648
Vicat Softening Point	98.0 °C @Thickness 6.35 mm	208 °F @Thickness 0.250 in	Rate B; ASTM D-1525