Chevron Phillips 5625 LDPE Case Shrink and Bundling Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips 5625 LDPE Case Shrink and Bundling Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: HomopolymerCharacteristics: Superior Impact Strength, Good Abrasion and Tear Resistance, Good Sealing Properties, No Slip, High Antiblock, Easy Openability, Medium Coefficient of FrictionApplications:Case Shrink Wrap, C&A Film and Container Liners, Bundling ApplicationsProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.0762 cm. Blow-Up Ratio 2:1.Film properties below based on film thickness of 31.8 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.922 g/cc	0.0333 lb/in³	ASTM D1505
Melt Flow	0.65 g/10 min	0.65 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Secant Modulus, MD	0.170 GPa	24.7 ksi	ASTM D882
Secant Modulus, TD	0.180 GPa	26.1 ksi	ASTM D882
Coefficient of Friction	0.50	0.50	ASTM D1894
Dart Drop	4.40 g/micron	112 g/mil	F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709

Optical Properties	Metric	English	Comments
Haze	8.5 %	8.5 %	ASTM D2457
Gloss	54 %	54 %	at 45°. ASTM D 2457
	85 %	85 %	at 60°. ASTM D 2457

Processing Properties	Metric	English	Comments
Melt Temperature	210 °C	410 °F