BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3WG6 HP BK 23210 30% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade with enhances flowability used e.g. for automobile manifold.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 |
| 0.0025 cm/cm | 0.0025 in/in | ISO 2577 | |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | ISO 2577 |
| 0.0065 cm/cm | 0.0065 in/in | ISO 2577 | |
| Melt Flow | 68 g/10 min @Load 5.00 kg, Temperature 275 °C |
68 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | DIN 58765 |
| Decomposition Temperature | >= 300 °C | >= 572 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feed Zone |
| Zone 2 | 270 °C | 518 °F | Compression |
| Zone 3 | 280 °C | 536 °F | Metering-zone |
| Zone 4 | 280 °C | 536 °F | Nozzle |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
| 280 °C | 536 °F | Optimal | |
| Mold Temperature | 80.0 °C | 176 °F | Optimal |
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK 23210 | |
| Commercial Status | Europe | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 201 PC
- SABIC Innovative Plastics Lexan® 925AU PC (Asia Pacific)
- Sumitomo Bakelite North America RX® 2-501N Mineral Filled Diallyl Phthalate
- SCG Chemicals EL-Leneâ„¢ H6670B High Density Polyethylene Film
- SCG Chemicals EL-Leneâ„¢ LD1905F Low Density Polyethylene Film
- A. Schulman PP 1692 Polypropylene High Impact Copolymer
- Daikin NEOFLON AC-5830 PFA Coating Powder, Gray
- Diamond Polymers DIAMALOY ABSPC 750 HF ABS/PC Alloy, Non-Halogen, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved