- Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT
Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Chang Chun Plastic Co. Ltd. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dowell Trading Company Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 - 1.43 g/cc | 0.0502 - 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.020 cm/cm | 0.0040 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 93 | 93 | ASTM D785 |
| Tensile Strength, Ultimate | 80.0 - 100 MPa | 11600 - 14500 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | ASTM D638 |
| Flexural Yield Strength | 130 - 150 MPa | 18900 - 21800 psi | ASTM D790 |
| Flexural Modulus | 4.00 - 5.00 GPa | 580 - 725 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 - 0.700 J/cm @Thickness 6.35 mm |
0.937 - 1.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/32 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz |
3.3 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| Arc Resistance | 129 sec | 129 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Pyrotek TS-82 Thermoset Electrical Insulation Product (Nema Grade: XXX)
- PolyOne Lubri-Tech™ AS-000/10T-2S ABS - 10% PTFE - 2% Silicone (discontinued **)
- Indium Corp. Indalloy 148 Pure Bismuth
- Metton LMR M1534 Liquid Molding Resin
- Isoflon PTFE + 60% Bronze Polytetrafluoroethylene with 60% Bronze
- SABIC Innovative Plastics ULTEM SF2350 PEI Blend
- Borealis Visico™ LE0540 Polyethylene Semiconductive Compound, Crosslinkable
- Hexcel® HexForce™ X8T196 Carbon Fabric
- Azoty Tarnow™ TARNOFORM KSI POM
- ATI Allegheny Ludlum AL 13-8™ H 1050 Precipitation Hardening Alloy, Heat Treated at 1050°F
Copyright © lookpolymers.com All Rights Reserved