Chang Chun Plastic PBT1100L General Purpose PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Chang Chun Plastic Co. Ltd. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chang Chun Plastic PBT1100L General Purpose PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dowell Trading Company Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.32 g/cc | 0.0470 - 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 - 90 | 85 - 90 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
| Elongation at Break | 120 - 180 % | 120 - 180 % | ASTM D638 |
| Flexural Yield Strength | 75.0 - 85.0 MPa | 10900 - 12300 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 - 0.600 J/cm @Thickness 6.35 mm |
0.937 - 1.12 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C @Temperature 20.0 °C |
50.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/32 in. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz |
3.3 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers G-2194
- LATI LATILUB 73/13-01M Polyoxymethylene Base (POM), 1% Molybdenum Disulfide Self Lubricating Plastic (Unv
- Huntsman DY 9577 Epoxy Accelerator
- Kotec Carbotex K-30F5 Polycarbonate, Wear Resistant
- ExxonMobil Label-Lyte™ 33LL247 OPP Film
- Chosun Refractories BCT-145 Acid-proof Castable
- Eurotec® Tecotek® PC43 GR003 TD70 PC, unfilled, flame retardant - halogen (RoHS compliant), impact modified, light grey
- Colorite Polymers 8512 Clear Injection Molding Vinyl Compound
- Bulk Molding Compounds BMC 845 Vinyl Ester Molding Compounds, 30% Glass-Filled
Copyright © lookpolymers.com All Rights Reserved