Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
Manufacturer | Carpenter Technology Corporation (Cartech) |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 718°C (1325°F)/8hr/AC to 621°C (1150°F)/8hr/AC.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.40 g/cc | 0.303 lb/in³ |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Brinell | 326 | 326 | Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement. |
Hardness, Knoop | 354 | 354 | Estimated from Rockwell C |
Hardness, Rockwell C | 35 | 35 | |
Hardness, Vickers | 341 | 341 | Estimated from Rockwell C |
Tensile Strength, Ultimate | 1220 MPa | 177000 psi | |
Tensile Strength, Yield | 827 MPa @Strain 0.200 % |
120000 psi @Strain 0.200 % |
|
Elongation at Break | 37 % | 37 % | In 4D |
Reduction of Area | 57 % | 57 % | |
Modulus of Elasticity | 207 GPa @Temperature 23.0 °C |
30000 ksi @Temperature 73.4 °F |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 12.6 µm/m-°C @Temperature 25.0 - 100 °C |
7.00 µin/in-°F @Temperature 77.0 - 212 °F |
|
13.4 µm/m-°C @Temperature 25.0 - 300 °C |
7.44 µin/in-°F @Temperature 77.0 - 572 °F |
||
14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
||
Specific Heat Capacity | 0.418 J/g-°C | 0.0999 BTU/lb-°F | |
Melting Point | 1257 - 1356 °C | 2295 - 2473 °F | |
Solidus | 1257 °C | 2295 °F | |
Liquidus | 1356 °C | 2473 °F |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Aluminum, Al | <= 0.35 % | <= 0.35 % | |
Carbon, C | <= 0.030 % | <= 0.030 % | |
Chromium, Cr | 19 - 22 % | 19 - 22 % | |
Iron, Fe | 5.0 % | 5.0 % | as remainder |
Manganese, Mn | <= 0.20 % | <= 0.20 % | |
Molybdenum, Mo | 7.0 - 9.5 % | 7.0 - 9.5 % | |
Nickel, Ni | 59 - 63 % | 59 - 63 % | |
Niobium, Nb (Columbium, Cb) | 2.75 - 4.0 % | 2.75 - 4.0 % | |
Phosphorous, P | <= 0.015 % | <= 0.015 % | |
Silicon, Si | <= 0.20 % | <= 0.20 % | |
Sulfur, S | <= 0.010 % | <= 0.010 % | |
Titanium, Ti | 1.0 - 1.6 % | 1.0 - 1.6 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0001299 ohm-cm | 0.0001299 ohm-cm |