- California Fine Wire Manganin 230 (Shunt) Copper, Manganese, and Nickel Resistance Wire
California Fine Wire Manganin 230 (Shunt) Copper, Manganese, and Nickel Resistance Wire
| Category | Metal , Electronic/Magnetic Alloy , Nonferrous Metal , Copper Alloy |
| Manufacturer | California Fine Wire |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | California Fine Wire Manganin 230 (Shunt) Copper, Manganese, and Nickel Resistance Wire.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
All values may vary dependent on specific design and usageNickel content modifiedCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.17 g/cc | 0.295 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 483 MPa | 70000 psi | Annealed |
| 1030 MPa | 150000 psi | Hard |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.7 µm/m-°C @Temperature 20.0 °C |
10.4 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 0.406 J/g-°C @Temperature 20.0 °C |
0.0970 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 19.8 W/m-K | 137 BTU-in/hr-ft²-°F | |
| Melting Point | 1020 °C | 1868 °F | |
| Maximum Service Temperature, Air | 200 °C | 392 °F | Operating Temperature |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 84 % | 84 % | |
| Manganese, Mn | 12 % | 12 % | |
| Nickel, Ni | 4.0 % | 4.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000382 ohm-cm | 0.0000382 ohm-cm | 3% tolerance on sizes below 0.02, 5% tolerance on sizes above 0.02 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Magnetic | None | |
| Temperature Coefficient of Resistance | ±0.000015 ohms/ohm-°C | 0-100°C |
| Thermal EMF vs. Copper | <+3 |
Users viewing this material also viewed the following:
- Kazanorgsintez OS-20 Textile Auxiliary Agent
- Taiwan Sheen Soon Sheenthane® AH-580 TPU for Hotmelt Adhesive
- Solvay ALKAMULS® PSMO 20 Surfactant
- Sumitomo Bakelite North America E 16521A Electrical Encapsulation Grade Epoxy
- A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene
- Unitika elitel UE3350 Polyester, Flake
- A. Schulman PP 1407H-01 Polypropylene High-Impact Polypropylene
- Daikin NEOFLON AP-231SH PFA Semiconductor Grade
- Azoty Tarnow™ Tarnamid® T-27 M Polyamide 6 - Improved Slip Properties
- ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets (discontinued **)
Copyright © lookpolymers.com All Rights Reserved