Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr

Category	Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer	Carpenter Technology Corporation (Cartech)
Trade Name	BioDur™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 1 hr.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting high strength, corrosion resistance, and wear resistance. BioDur CCM Plus alloy is a wrought powder metallurgy product produced by vacuum induction melting (VIM) followed by inert gas atomization and hot isostatic pressing to produce 100% dense billets. These billets are then processed by conventional steel-making practices to make finished products.BioDur™ and CCM Plus™ are trademarks of Carpenter Technology Corporation.

Physical Properties	Metric	English	Comments
Density	8.28 g/cc	0.299 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	389	389	Estimated from Rockwell C for Brinell test with 3000 kg load, 10 mm ball.
Hardness, Knoop	425	425	Estimated from Rockwell C
Hardness, Rockwell C	42	42
Hardness, Vickers	407	407	Estimated from Rockwell C
Tensile Strength, Ultimate	1351 MPa	195900 psi
Tensile Strength, Yield	882 MPa @Strain 0.200 %	128000 psi @Strain 0.200 %
Elongation at Break	22 %	22 %	in 4D
Reduction of Area	18 %	18 %

Thermal Properties	Metric	English
CTE, linear	12.8 µm/m-°C @Temperature 0.000 - 100 °C	7.11 µin/in-°F @Temperature 32.0 - 212 °F
	13.1 µm/m-°C @Temperature 25.0 - 300 °C	7.30 µin/in-°F @Temperature 77.0 - 572 °F
	14.7 µm/m-°C @Temperature 25.0 - 700 °C	8.18 µin/in-°F @Temperature 77.0 - 1290 °F
	16.92 µm/m-°C @Temperature 25.0 - 1000 °C	9.400 µin/in-°F @Temperature 77.0 - 1830 °F
Specific Heat Capacity	0.452 J/g-°C @Temperature 23.0 °C	0.108 BTU/lb-°F @Temperature 73.4 °F
	0.590 J/g-°C @Temperature 600 °C	0.141 BTU/lb-°F @Temperature 1110 °F
	0.673 J/g-°C @Temperature 1100 °C	0.161 BTU/lb-°F @Temperature 2010 °F
Thermal Conductivity	12.766 W/m-K @Temperature 23.0 °C	88.596 BTU-in/hr-ft²-°F @Temperature 73.4 °F
	25.264 W/m-K @Temperature 600 °C	175.33 BTU-in/hr-ft²-°F @Temperature 1110 °F
	35.022 W/m-K @Temperature 1177 °C	243.05 BTU-in/hr-ft²-°F @Temperature 2151 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	0.20 - 0.30 %	0.20 - 0.30 %
Chromium, Cr	26 - 30 %	26 - 30 %
Cobalt, Co	66 %	66 %	as remainder
Molybdenum, Mo	5.0 - 7.0 %	5.0 - 7.0 %
Nitrogen, N	0.15 - 0.20 %	0.15 - 0.20 %