SABIC Innovative Plastics LNP THERMOTUF QX01581H PA 6/10 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF QX01581H PA 6/10 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 134 MPa | 19400 psi | ISO 527 |
| 139 MPa | 20200 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| 3.6 % | 3.6 % | ISO 527 | |
| Tensile Modulus | 7.88 GPa | 1140 ksi | 1 mm/min; ISO 527 |
| 8.48 GPa | 1230 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| 208 MPa | 30200 psi | ISO 178 | |
| Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
| 7.25 GPa | 1050 ksi | ISO 178 | |
| Izod Impact, Notched | 3.57 J/cm | 6.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.58 J/cm | 21.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 32.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 88.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Magyar Aluminum ALO-DF223 Alumina
- Aardvark Polymers Aarlon® 4055FR PA 6/6 Rotational Molding Resin
- SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-LOY AF3029U ABS (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Diamond Polymers NPP11-0242 Polyethylene
- CIMBAR Suspengel™ 30 High Purity Bentonite, Industrial Grade
- PolyOne Synprene® IT 702 Thermoplastic Elastomer - SBC, Mineral Filled (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N990 Filler
- SABIC Innovative Plastics LNP THERMOCOMP JF004L PES
Copyright © lookpolymers.com All Rights Reserved