CTC X-PRO TF 1020 GP Polypropylene Homopolymer, 20% Talc Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer	CTC (Composite Technologies)
Trade Name	X-PRO
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	CTC X-PRO TF 1020 GP Polypropylene Homopolymer, 20% Talc Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

X-PRO TF 1020 GP is a 20% talc reinforced polypropylene homopolymer. It has applications in general purpose industrial, automotive, consumer, and construction.Data provided by Composite Technologies (CTC).

Physical Properties	Metric	English	Comments
Melt Flow	10 g/10 min	10 g/10 min	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	13.8 MPa	2000 psi	ISO 527-1/2
Flexural Modulus	1.72 GPa	250 ksi	0.05 in/min; ISO 178
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ISO 180/1eA

Processing Properties	Metric	English
Rear Barrel Temperature	204 - 216 °C	400 - 420 °F
Middle Barrel Temperature	216 - 227 °C	420 - 440 °F
Front Barrel Temperature	227 - 238 °C	440 - 460 °F
Melt Temperature	227 - 238 °C	440 - 460 °F
Mold Temperature	26.7 - 60.0 °C	80.0 - 140 °F
Back Pressure	0.689 - 1.03 MPa	100 - 150 psi
Clamp Pressure	27.6 - 34.5 MPa	4000 - 5000 psi

Descriptive Properties	Value	Comments
Boost Pressure (psi)	750-1500
Hold Pressure	50 - 75% of Boost
Screw Speed	Fast