- CP-Polymer-Technik Wellamid® 6600 CF20 HWCP 20% Carbon Fiber Nylon 66, Heat Stabilized, Conditioned
CP-Polymer-Technik Wellamid® 6600 CF20 HWCP 20% Carbon Fiber Nylon 66, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Carbon Fiber Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6600 CF20 HWCP 20% Carbon Fiber Nylon 66, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 - 2.5 % | 2.0 - 2.5 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 12.5 GPa | 1810 ksi | ISO 527 |
| Charpy Impact Unnotched | 7.20 J/cm² @Temperature 23.0 °C |
34.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | Kofler |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- LATI LARPEEK 10 G/50 50% Glass Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Ineos Nova FX510 Super High Impact Polystyrene (discontinued **)
- NOVA Chemicals Novapol® LE-0520-AM LDPE Extrusion Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 80/TF/22/NT Polyacetal-copolymer, with PTFE
- Fine Organics FINALUX G 732 Lubricant Additive
- Inno-Comp INNOPOL® CS 1-5820 20% Glass-Fiber-Filled Polypropylene Homopolymer
- Heatbath/Park #800 High Speed Hardening Salt
- Techmer ES Elastoblend® PA6/6 IM L W Nylon 66
- Bohler-Uddeholm UDDEHOLM CORRAX® Precipitation Hardening Stainless Mold Steel
Copyright © lookpolymers.com All Rights Reserved