Braskem LL218 Cast Film Extrusion Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LL218 Cast Film Extrusion Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D1505/D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 1310 % | 1310 % | ASTM D882 |
| Film Elongation at Break, TD | 1560 % | 1560 % | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 190 g | 190 g | gF; ASTM D1922 |
| Dart Drop Test | 100 g | 0.221 lb | g/F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 54 % @Thickness 0.0250 mm |
54 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 24 % @Thickness 0.0250 mm |
24 % @Thickness 0.000984 in |
60°; ASTM D2457 |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CR750CL-02 Polypropylene, Random Copolymer, NX-8000 based
- SABIC Innovative Plastics Lexan® 945A PC
- Mitsui Arlenâ„¢ C230 30% Glass Fiber-Reinforced Modified Nylon 6T (DAM)
- Heatbath/Park Marquench Oil M
- SABIC Innovative Plastics LNP THERMOCOMP RC006 PA 66
- Bapolene® 0760 Polyethylene, Blow Molding Grade
- Arlon R37642R062 0.062" (1.57 mm) Cured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Braskem IE59U3 HDPE Injection Molding Polyethylene Homopolymer
- Johnson Matthey JM PA Soft Solder Flux
- Lehmann & Voss LUVOCOM® 1105-7096 PEEK, with carbon fiber, easy flowing
Copyright © lookpolymers.com All Rights Reserved