Braskem H 604 Thermoforming & Extrusion Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem H 604 Thermoforming & Extrusion Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent packaging for food; Flat and corrugated sheets for school and office folders.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.905 g/cc | 0.905 g/cc | ASTM D792 |
| Melt Flow | 1.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Yield | 12 % | 12 % | ASTM D638 |
| Flexural Modulus, 1% Secant | 1350 MPa | 196000 psi | ASTM D790A |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ASTM D648 |
| Vicat Softening Point | 146 °C | 295 °F | 10 N; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 27 % @Thickness 1.00 mm |
27 % @Thickness 0.0394 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1332L Polycarbonate, UV Stabilized, Unreinforced
- DuPont™ Surlyn® 9970 Ionomer Resin, Zinc (discontinued **)
- Kolon KOCETAL® CF702 Conductive Grade Acetal Resin
- Sharadaa Ceramics Sharada RFC-80 Gel Bonded Castables
- SABIC Innovative Plastics LNP THERMOCOMP PH1100B PA 6
- Solvay Polishing Opalineâ„¢
- A. Schulman POLYFORT™ PP 2175HU-31 High Flow Copolymer Polypropylene
- Fainplast Compounds PMP 81 Flexible PVC, Extrusion Modified with PU
- Abatron L060421-1 Heat-Resistant (-75~400°F) Non-Flammable Silicone Rubber
- Custom Resins Vexel™ 4200 RD PBT; 30% Glass Filler (discontinued **)
Copyright © lookpolymers.com All Rights Reserved