Braskem BF 0323/12 HC LDPE Blown Film Extrusion Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem BF 0323/12 HC LDPE Blown Film Extrusion Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: BF0323/12 is a high molecular weight LDPE produced under high pressure technology. Films obtained with this product show outstanding optical properties, excellent mechanical properties, and good shrinkage.38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Shrink films; automatic packaging of liquids products (FFS). Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.32 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.32 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ASTM D638 |
| Film Elongation at Break, MD | 390 % | 390 % | ASTM D882 |
| Film Elongation at Break, TD | 1040 % | 1040 % | ASTM D882 |
| Elmendorf Tear Strength, TD | 100 g/micron | 2540 g/mil | F50; ASTM D1922 |
| Dart Drop | 100 g/micron | 2540 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 83 % | 83 % | 60° angle; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 110 °C | 230 °F | |
| Die Temperature | 190 °C | 374 °F | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Antiblock and Slip | |
| Minimum Recommended Thickness | 50 µm |
Users viewing this material also viewed the following:
- Mykroy/Mycalex MM 400 Machining Grade Glass-bonded Mica Composite
- RheTech Products T28P100-01EG 28% Talc Reinforced Polypropylene, Black, Extrusion Grade
- Polymer Resources AC-GP2-UV Acetal Copolymer, Medium Flow, UV-stabilized
- H.C. Starck Amperit® 825.1 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Karina E 360-IS-SI-SD Ivory PVC Compound
- SPS Guang Zhou FILLMAâ„¢ 5002F30C Mineral Filled Polypropylene
- Teknor Apex APEX® 94-A0098A-85 Polyvinyl Chloride, Flexible
- Teknor Apex APEX® 02-A0310A-107 Polyvinyl Chloride, Semi-Rigid
- Aclo Accucomp Polyethylene HD0200L High Density
Copyright © lookpolymers.com All Rights Reserved