Borealis HD601CF Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Borealis
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis HD601CF Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HD601CF is a homopolymer film resin, suitable for the manufacturing of unoriented film on chill roll process. Applications: metallisable cast film, inner layer in co extrusion, textile packaging film, food packaging, lamination films, stationary films, blending with formulated grades for additive adjustments, and manufacturing of unoriented film for producers who wish to add their own slip/antiblock/antistatic additive package. Additives: HD601CF Free of slip and antiblock and without CaStearate.Information provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.900 - 0.910 g/cc	0.0325 - 0.0329 lb/in³	base resin; ISO 1183
Melt Flow	8.0 g/10 min @Load 2.16 kg, Temperature 230 °C	8.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 - 700 %	500 - 700 %	ISO 527-3
Film Elongation at Break, TD	500 - 700 %	500 - 700 %	ISO 527-3
Tensile Modulus	0.650 - 0.750 GPa	94.3 - 109 ksi	MD/TD; ISO 527-3
Flexural Modulus	1.45 GPa	210 ksi	ISO 178
Dart Drop, Total Energy	12.0 J @Thickness 0.0500 mm	8.85 ft-lb @Thickness 0.00197 in	1100N; ISO 7765-2
Coefficient of Friction	>= 0.70	>= 0.70	film to film; ISO 8295
Film Tensile Strength at Break, MD	30.0 - 50.0 MPa	4350 - 7250 psi	ISO 527-3
Film Tensile Strength at Break, TD	25.0 - 45.0 MPa	3630 - 6530 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	162 - 166 °C	324 - 331 °F	DSC; ISO 3146
Vicat Softening Point	154 °C @Load 1.02 kg	309 °F @Load 2.25 lb	A50; ISO 306

Optical Properties	Metric	English	Comments
Haze	<= 2.0 %	<= 2.0 %	ASTM D1003
Gloss	>= 120 %	>= 120 %	20° of arc; ASTM D2457

Descriptive Properties	Value	Comments
Metal Adhesion (tape test)	Excellent