Chosun Refractories HSC-18RA Dense and High-Strength Castable, Superdense
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-18RA Dense and High-Strength Castable, Superdense.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.01962 GPa @Temperature 110 °C, Time 86400 sec |
2.846 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.024525 GPa @Temperature 1000 °C, Time 10800 sec |
3.5571 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.027468 GPa @Temperature 1500 °C, Time 10800 sec |
3.9840 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 98.1 MPa @Temperature 110 °C, Time 86400 sec |
14200 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 108 MPa @Temperature 1000 °C, Time 10800 sec |
15600 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 127 MPa @Temperature 1500 °C, Time 10800 sec |
18500 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.300 % @Temperature 1500 °C, Time 10800 sec |
-0.300 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 90 % | 90 % | |
| CaO | 2.0 % | 2.0 % | |
| SiC | 5.0 % | 5.0 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating | |
| Material Required for Estimating(kg/?) | 3,200 | |
| Water Required for Casting(%) | 4.0 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific)
- Honeywell ACLAR® 33C (0.75 mil) Copolymer Film (discontinued **)
- Lanxess Durethan® BCF 30 X H2.0 901510 Nylon 6, 30% Glass + Carbon Fiber
- Momentive Performance Materials IS803 One-Component, Paste Consistency Silicone Rubber Adhesive Sealant, Black
- SABIC Innovative Plastics LNP LUBRICOMP DX00714H PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP MB006SXP PP (Europe-Africa-Middle East)
- Excalibar NewBar™ API Barite BaSO4 Powder
- Arlon 55581R028 0.028" (0.711 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M 6035PC 12048 Polyurethane Foam Tape (20 lb./ft3 (320 kg/m3) Series)
Copyright © lookpolymers.com All Rights Reserved