Bhansali Engineering Abstron KU-650 ABS Super Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Bhansali Engineering |
| Trade Name | Abstron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Abstron KU-650 ABS Super Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Heat Resistant Grades with Better Flow characteristicInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.045 g/cc | 0.03775 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D-955 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D-785 |
| Tensile Strength, Yield | 43.15 MPa @Thickness 3.20 mm |
6258 psi @Thickness 0.126 in |
Type 1, 5 mm/min; ASTM D-638 |
| Flexural Yield Strength | 66.7 MPa @Thickness 6.40 mm |
9670 psi @Thickness 0.252 in |
ASTM D-790 |
| Flexural Modulus | 2.16 GPa @Thickness 6.40 mm |
313 ksi @Thickness 0.252 in |
ASTM D-790 |
| Izod Impact, Notched | 1.3725 J/cm @Thickness 6.40 mm |
2.5713 ft-lb/in @Thickness 0.252 in |
ASTM D-256 |
| 1.7647 J/cm @Thickness 3.20 mm |
3.3060 ft-lb/in @Thickness 0.126 in |
ASTM D-256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Method A - Annealed; ASTM D-648 |
| Vicat Softening Point | 122 °C | 252 °F | Method B; ASTM D-1525 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL-94 |
Users viewing this material also viewed the following:
- MV Labs SC300 Sc2(CO3)3.xH2O Scandium carbonate
- Osprey Metals 316L/MA Master Alloy Stainless Steel Powder (Grade 90% - 16)
- SABIC Innovative Plastics Cycolac® MG29 ABS
- Nilit FRIANYL B63 H-KV30 Nylon 6 for injection molding, 30% glass ball reinforced
- Mitsui APELâ„¢ APL6509T Cyclo Olefin Copolymer (COC)
- Dow SPECTRIM™ 50B-S Polyol
- Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
- Arkema Group Pebax® Rnew 40R53 SP 01 Polyether Block Amide (PEBA)
- 3M Scotchcal™ ElectroCut™ 7725-22 Graphic Film
- SABIC Innovative Plastics Lexan® 943 PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved