- Barlog Plastics KEBAFORM C 2527 POM Copolymer, 25% glass fiber reinforced
Barlog Plastics KEBAFORM C 2527 POM Copolymer, 25% glass fiber reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 2527 POM Copolymer, 25% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POM-GF25Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | similar to ISO 62 test |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM-GF25 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ BIO 5180D-E0014 Thermoplastic Elastomer (TPE)
- Nye Lubricants UniFlor 8512SB (UF) Synthetic Oil
- Polimeri Europa Greenflex® FD 20 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
- Kazanorgsintez 102-12K Cable Composition Based on Low Density Polyethylene
- Isoflon PTFE + 50% Stainless Steel (AISI 316 L) Polytetrafluoroethylene with 50% INOX Stainless Steel
- SABIC Innovative Plastics Xenoy® 1760T PBT+PC (Europe-Africa-Middle East)
- Teknor Apex Sarlink® 3145D Thermoplastic Elastomer
- Zeon Chemicals Zeonor® 1060R Cyclo Olefin Polymer
- BASF Elastollan® 1160D Polyether Type Polyurethane Elastomer
- BASF Ultramid® B3EG3 15% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved